Vol.:(0123456789) https://doi.org/10.1007/s10008-022-05142-w ORIGINAL PAPER Aqueous spray‑drying synthesis of alluaudite Na2+2xFe2−x(SO4)3 sodium insertion material: studies of electrochemical activity, thermodynamic stability, and humidity‑induced phase transition Pubali Barman1 · Debasmita Dwibedi1,2 · K. Jayanthi3 · Sher Singh Meena4 · Supreeth Nagendran5,6 · Alexandra Navrotsky3 · Prabeer Barpanda1,7 Received: 8 February 2022 / Revised: 16 February 2022 / Accepted: 21 February 2022 © The Author(s) 2022 Abstract In pursuit of high-energy density sodium insertion materials, polyanionic frameworks can be designed with tuneable high- voltage operation stemming from inductive effect. Alluaudite Na2Fe2(SO4)3 polysulfate forms one such earth-abundant compound registering the highest Fe3+/Fe2+ redox potential (ca. 3.8 V vs. Na/Na+). While this SO4-based system exhibits high voltage operation, it is prone to thermal decomposition and moisture attack leading to hydrated derivatives, making its synthesis cumbersome. Also, the Na–Fe–S–O quaternary system is rich with (anhydrous to hydrated) phase transitions. Herein, we demonstrate scalable aqueous-based spray drying synthesis of alluaudite Na2+2xFe2−x(SO4)3 sodium insertion material involving the formation of bloedite Na2Fe(SO4)2·4H2O as an intermediate phase. Moreover, a reversible phase transition from alluaudite to bloedite under controlled conditions of temperature and relative humidity is reported for the first time. Thermochemistry measurements revealed the enthalpies of formation (ΔH°f) of alluaudite and bloedite are exo- thermic. Hydrated bloedite (ΔH°f = −117.16 ± 1.10 kJ/mol) was found to be significantly more energetically stable than anhydrous alluaudite (ΔH°f = −11.76 ± 1.25 kJ/mol). The calorimetric data support the observed synthesis and transformation (hydration-dehydration) pathways. Spray drying route led to spherical morphology delivering capacity ~80 mAh/g. Spray drying can be extended for rapid economic synthesis of sulfate class of battery materials. Keywords Sodium-ion battery · Cathode · Alluaudite · Capacity · Phase transition Introduction Rechargeable batteries rule the energy storage sector in the twenty-first century. Batteries broadly cater to two kinds of applications: volume/weight-restricted application like electronic gadgets/electric automobiles and volume/weight- independent usages like stationary grid storage. While lith- ium-ion batteries (LIBs) are irreplaceable for the former category, the latter can be propelled by economic sodium- ion batteries (SIBs) [1]. To realize practical SIBs with high energy density, suites of oxides and polyanionic insertion materials have been unveiled. While oxides can deliver high capacity, polyanionic compounds are particularly known for their high-voltage operation, thermal/chemical stability, and operational safety. Particularly exploiting the inductive effect, simply by changing the electronegative polyanionic moieties (S > W > P > Mo), the working potential of the cath- ode material can be tuned [2, 3]. On another note, material economy can be realized by combining earth-abundant alkali Pubali Barman and Debasmita Dwibedi contributed equally to this work. * Prabeer Barpanda prabeer@iisc.ac.in 1 Faraday Materials Laboratory (FaMaL), Materials Research Center, Indian Institute of Science, Bangalore 560012, India 2 Department of Chemical System Engineering, The University of Tokyo, 7-3-1 Hongo, Bunkyo-ku, Tokyo 113-8656, Japan 3 School of Molecular Sciences and Navrotsky Eyring Center for Materials of the Universe, Arizona State University, Tempe, AZ 85287, USA 4 Solid State Physics Division, Bhabha Atomic Research Centre, Mumbai 400085, India 5 Department of Chemistry, Central College, Bangalore University, Bangalore 560001, India 6 Department of Chemistry, University of Cambridge, Lensfield Road, Cambridge CB2 1EW, UK 7 Helmholtz Institut Ulm (HIU), Helmholtzstrasse 11, Ulm 89081, Germany / Published online: 4 March 2022 Journal of Solid State Electrochemistry (2022) 26:1941–1950 1 3 (e.g., Na) and transition metal (e.g., Fe) chemistry. Some such examples are NaFeO2, Nax[Fe1/2Mn1/2]O2, NaFePO4, Na2FePO4F, Na2FeP2O7, and Na4Fe3(PO4)2(P2O7), each operating around 3 V [1, 4]. To enhance the overall nomi- nal voltage of polyanionic compounds, the phosphate group can be substituted by highly electronegative sulfate group (SO42−) [2, 5]. Using this strategy, in 2014, Yamada group reported sulfate-based alluaudite class of high-voltage cath- ode material [6]. Alluaudites, named after its discoverer Franҫois Allu- aud II, are a group of alkali metal phosphate–based natu- rally occurring minerals having open frameworks as well as broad tunnels for easy alkali ion passage [7]. The gen- eral formula of alluaudite-based materials can be written as A (1)A(2)M(1)M(2)2(XO4)3, where A denotes the alkali ions, M denotes the transition metal ions, and X could be S, P, As, V, Mo, or W [8]. A and M(1) sites are occupied by monova- lent (Na+, Li+) or divalent cations (Ca2+, Mg2+) while the M(2) site can be filled with divalent (Mn2+, Fe2+) or trivalent cations (Mn3+, Fe3+, In3+). The MO6 octahedra and XO4 tetrahedra are connected to form two tunnels along the c direction within the structure. A(1) and A(2) sites, occupied by alkali ions, are situated inside these tunnels capable of ion mobility within the alluaudite framework. Delmas group reported the first alluaudite type cathode NaMnFe2(PO4)3 for SIBs albeit with poor activity as well as low working voltage [9]. To overcome the voltage issue, Yamada group reported the first SO42−-based alluaudite material Na2Fe2(SO4)3 reg- istering the highest Fe3+/Fe2+ redox potential (ca. 3.8 V vs. Na/Na+). This discovery ushered further research on Na2+2xM2−x(SO4)3 alluaudite class of SIB cathode materi- als [10–15]. While these sulfate-based alluaudites offer high working voltage and energy density, their syntheses remain cumbersome. While the solid-state route warrants prolonged mechanical milling and annealing duration, ionothermal route can be expensive. Most synthesis routes cannot directly use commercially available FeSO4·7H2O precursor, but instead use its anhydrous derivatives FeSO4·nH2O (n = 0.1). In the present work, we report spray-drying synthesis (SDS) as a solvothermal method for scalable synthesis of alluaudite Na2+2xFe2−x(SO4)3 insertion material directly using commercial FeSO4·7H2O precursor. This two-step route involves the formation of bloedite Na2Fe(SO4)2·4H2O as an intermediate phase followed by its transition to the alluaudite target material. SDS facilitates the formation of spherical morphology along with restricted annealing duration. We further report the use of X-ray diffraction under controlled condition of relative humidity (RH-XRD) for gauging potential moisture attack on alluaudite. Upon varying humidity from 10 to 90%, a systematic alluaudite- to-bloedite phase transition was observed, while opposite phase transition (i.e., bloedite-to-alluaudite) was noticed upon annealing. The thermodynamics of formation and dehydration, measured by calorimetric techniques, confirms the stability of the hydrated bloedite phase and the observed transformation at high temperature. The SDS prepared allu- audite can deliver 77% of the theoretical capacity retaining high redox potential without any cathode optimization or conductive additives. Materials and methods Synthesis The target alluaudite was prepared by solution- based spray-drying synthesis (SDS) method using a Büchi B-90 spray dryer connected to a peristaltic pump. A uni- form aqueous slurry was prepared containing a stoichio- metric mixture of commercial precursors Na2SO4 (SDFCL, 99.5%) and FeSO4·7H2O (SDFCL, 99.5%). Unlike the clas- sical solid-state route, the incorporation of aqueous medium assured atomic-level mixing and labile ionic diffusion [16]. Spray drying is a method of producing dry powders from precursor solution by atomization in small droplets (spray) and evaporation (drying) at the droplet surface at increased temperature. Here, the precursor slurry was passed through the nozzle of the spray dryer, leading to nebulization and rapid transformation into solids upon exposure of tiny drop- lets with hot air. For spray drying, the inlet and outlet tem- peratures were maintained at 200 °C and 80 °C respectively. The spray-dried powder was collected using cyclone sepa- rators, bag filters, electrostatic precipitator, and wet scrub- bers. This intermediate dried complex was pelletized and annealed at 350 °C for 6–8 h in a tubular furnace maintained under steady argon flow. Ascorbic acid (C6H8O6, Sigma, 99%) can be optionally added in the initial slurry to facilitate the formation of in situ carbon coating on the target mate- rial. The SDS route can yield desired materials either at low annealing temperature and/or shorter annealing duration, which in turn yields particles with minimal grain growth, facilitating superior electrochemical activity. Structural and physical characterization The powder X-ray diffraction (PXRD) patterns were acquired with a PANa- lytical Empyrean X-ray diffractometer equipped with a Cu Kα source (λ1 = 1.5405 Å, λ2 = 1.5443 Å) operating at 40 kV/30 mA. Rietveld analysis was performed using GSAS-I program with EXPGUI graphical interface [17–19]. The background, scale factor, lattice parameter, profile func- tions, and phase parameters were refined. Crystal structures were illustrated using the VESTA-3 software [20]. To probe the material stability upon moisture exposure, in situ XRD patterns were collected with a Bruker D8 Advance X-ray diffractometer (Cu Kα source, λ1 = 1.5405 Å, λ2 = 1.5443 Å, operating at 40 kV/30 mA) equipped with an Anton Paar CHC plus+ humidity chamber attachment with water inlet/ outlet. XRD patterns were collected after exposing the 1942 Journal of Solid State Electrochemistry (2022) 26:1941–1950 1 3 sample to various degrees of humidity (RH = 10% to 90%). Thermal analysis (TGA–DSC) of ~20 mg of the interme- diate compound was conducted with a Mettler Toledo instrument in the temperature range of 25–400 °C (under steady nitrogen flow) with a heating rate of 5 °C/min. Fou- rier transform infrared (FTIR) spectrum was collected with a PerkinElmer instrument in attenuated total reflectance (ATR) mode within the spectral range of 4000–650  cm−1. Raman spectra were recorded with a Horiba Jobin Yvon HR- Raman-123 MicroPL spectrometer with a green laser source (λ = 519 nm) to check the presence of carbon coating. Particle morphology was inspected by a Carl Zeiss Ultra55 field emission scanning electron microscope (FESEM, tung- sten source) operating at 0.1–30 kV. Gold sputtering was conducted on the powder sample, sprinkled over a double- sided carbon tape, for 120 s. Selected area electron diffrac- tion (SAED) pattern and the high-resolution transmission electron microscopy (HRTEM) images were obtained by a Titan Themis (Thermo-FEI, at 300 kV) transmission elec- tron microscope. For the TEM study, the powder sample was dispersed in absolute ethanol and was drop-casted on a holey carbon-copper grid. Elemental distribution was detected using an EDS analyzer equipped with the aforementioned TEM instrument. Mössbauer measurements Ambient temperature Mössbauer spectra (MS) were recorded with a conventional spectrom- eter with 57Co source in Rh matrix of 3 mCi operating in constant acceleration mode in transmission geometry. They were analyzed using the WinNormos site fit program. The calibration of the velocity scale was done by using an enriched α-57Fe metal foil. The isomer shift values are rela- tive to Fe metal foil (δ = 0.0 mm/s). Mössbauer spectra of both the spray-dried intermediate and the desired alluaudite phase were fitted with four symmetric doublets. Thermochemistry study PXRD and TG-DSC measurements were performed before and after the calorimetric measure- ment to detect any possible decomposition and to check for adsorbed water on the sample due to exposure in the ambi- ent atmosphere prior to solution calorimetric experiments. Dissolution enthalpy of Na2.27Fe1.86(SO4)3 in 5 N HCl was measured using both CSC 4400 isothermal (with IMC data acquisition software) and Hart Scientific (with Labview software) microcalorimeters with mechanical stirring of the samples and reagents at 25 °C. The calorimeters were cali- brated with KCl (NIST standard reference material) by dis- solving 15 mg pellets in 25 g of water at 25 °C. The solution enthalpy of this reference concentration (0.008 mol  kg−1), deduced from the literature and the enthalpy of dilution measurements [21], was used to obtain the calorimeter cali- bration factor. In a typical calorimetric run, 6 − 8 mg of the sample was pressed into a pellet and then dropped into 25 g of 5 N HCl placed in the sample chamber of the calorimeter. The sample dissolution causes heat flow due to temperature difference and is recorded as a microvolt calorimetric signal. The inte- grated area under the recorded microwatt signal relative to a linear baseline corresponds to the total heat effect which on conversion into joules with KCl calibration corresponds to the enthalpy of sample dissolution (ΔHds). An appropri- ate thermochemical cycle based on Hess’ law (difference in the heat of solution of products and reactants) was used to calculate the enthalpy of formation. This methodology is essentially the same as that used in prior studies [22]. Electrochemical characterization For electrode performance analysis, the working electrode was prepared from an intimate slurry containing 70 wt% of active material, 20 wt% of carbon black (Super-P) (Alfa Aesar), and 10 wt% polyvinylidene fluo- ride (PVDF) (Sigma Aldrich) binder in a minimal amount of N-methyl-2-pyrrolidone (NMP) (Sigma Aldrich) solvent. This slurry was uniformly coated on an Al foil acting as current collector followed by a vacuum drying at 120 °C for 12 h to remove the NMP. Circular disks (acting as working electrode) were punched with active material loading ~ 3–5 mg/cm2. CR2032 type coin cells were assembled inside an Ar-filled glove box (MBraun LabStar GmbH, O2 and H2O < 0.5 ppm) to avoid any moisture contamination. The working electrode and sodium metal foil (as counter electrode) were separated by a sheet of Whatman GF/C glass fiber separator soaked with 1 M NaPF6 in ethylene carbonate/diethyl carbonate (EC:DEC; 1:1 vol) electrolyte (battery grade, Kishida Chemicals). The electrochemical testing was performed (at 25 °C) using the Neware BTS-4000 battery tester in the potential window of 2–4.5 V at a rate of C/20 (1C = 100 mAh/g). Result and discussions While the alluaudite Na2+2xFe2−x(SO4)3 offers high energy density–powered by its 3.8  V activity along with fast kinetics, the presence of SO4 moieties makes it moisture sensitive and prone to thermal decomposition at tempera- ture > 450 °C. The sulfate compounds can be air-sensitive resulting in a poor electrochemical performance and structural stability. Thus, classical solid-state and aqueous solvothermal routes are ruled out. On another note, the Na–Fe–S–O quaternary system is rich with several inter- mediate phases and their hydrated derivatives like krohnkite [Na2Fe(SO4)2·2H2O], bloedite [Na2Fe(SO4)2·4H2O], and vanthoffite [Na6Fe(SO4)4], which are thermodynami- cally more stable than (off) stoichiometric alluaudites [Na2+2xFe2−x(SO4)3]. Therefore, apart from the solid-state (dry) route, alluaudite has been prepared by non-aqueous 1943Journal of Solid State Electrochemistry (2022) 26:1941–1950 1 3 solvothermal (e.g., hydrophobic ionic liquid) route [14] and indirect (dehydration) synthesis using bloedite [23]. In addition, the complexity in alluaudite synthesis arises from the Fe precursor FeSO4·7H2O (melanterite), which can con- vert to various anhydrous derivatives such as FeSO4·6H2O (ferrohexahydrite), FeSO4·5H2O (siderotil), FeSO4·4H2O (rozenite), FeSO4·H2O (szomolnokite), and anhydrous FeSO4 upon annealing. Further, it can convert to various hydrated derivatives like Fe5(SO4)6(OH)2·20H2O (copia- pite) and Fe2(SO4)3·11H2O (quenstedtite) etc. [24]. All these derivatives offer varied reaction kinetics for alluaudite formation making its synthesis tricky. Here, two-step spray drying synthesis [15] was implemented for preparation of target alluaudite having twin benefits of using aqueous (wet chemistry) reacting media and direct use of widely available FeSO4·7H2O precursor. Na Fe S a b a b Na Fe S -4 -2 0 2 4 Tr an sm itt an ce (a .u ) Exp. data Fitted data Doublet 1 (Fe2+) Doublet 2 (Fe2+) Doublet 3 (Fe2+) Doublet 4 (Fe2+) Velocity (mm/s) -4 -2 0 2 4 Exp. data Fitted data Doublet 1 (Fe2+) Doublet 2 (Fe3+) Doublet 3 (Fe2+) Doublet 4 (Fe2+) Velocity (mm/s) Tr an sm itt an ce (a .u ) Bloedite Alluaudite H2O * * * Fig. 1 Comparative X-ray diffraction patterns and corresponding Mössbauer spectra of (top) spray drying–induced intermediate prod- uct (bloedite) and (bottom) final alluaudite Na2.27Fe1.86(SO4)3 mate- rial after annealing at 350 °C for 6–8 h. The intermediate product was found to be majorly bloedite Na2Fe(SO4)2·4H2O with few unidenti- fied peaks marked by asterisk marks. The corresponding structures are shown in the insets. In both cases, Mössbauer spectra confirm the presence of mostly Fe2+ species Fig. 2 Rietveld refined XRD powder diffraction pattern of spray drying prepared alluaudite material. The experimental data points (red dots), calcu- lated patterns (black line), their difference (blue line), and the Bragg peaks [violet ticks for Na2.27Fe1.86(SO4)3, green ticks for α-FeSO4 and pink ticks for Na6Fe(SO4)4] are shown. Small amount of thermodynamically stable α-FeSO4 and vanthoffite Na6Fe(SO4)4 impurities were noticed, which are structurally illustrated in the inset in the Na2SO4-FeSO4 binary system 1944 Journal of Solid State Electrochemistry (2022) 26:1941–1950 1 3 Spray drying–induced nebulized precursor solution, where each nebula can be thought of as a spherical “nano- reactor,” quickly transformed to an intermediate complex upon exposure to hot air. This intermediate complex was found to consist of majorly bloedite Na2Fe(SO4)2·4H2O phase (Fig. 1). It comes as no surprise as bloedite is a sta- ble complex in the Na2SO4–FeSO4 binary system. Thermal analysis of this spray-dried intermediate complex revealed a series of endothermic peaks with no weight loss after 300 °C (Fig. S1, ESI). Taking a hint from the thermal analysis, the intermediate complex was annealed at 350 °C for 6-8 h (in Ar flow) involving dehydration to yield the desired alluau- dite phase. Rietveld analysis of the final material confirmed that major diffraction peaks can be indexed to the alluau- dite phase (97.01%) with minor stable secondary phases like α-FeSO4 (1.98%) and vanthoffite Na6Fe(SO4)4 (1.01%) (Fig. 2). Using the model structure proposed by Oyama et al. [13], the atomic positions, occupancy, and thermal param- eters of Na, Fe, S, and O atoms were refined to fit the major peaks. Rietveld refinement confirmed the formation of an off-stoichiometric Na2.27Fe1.86(SO4)3 alluaudite material crystallizing in monoclinic structure (s.g. C2/c) (Table S1, ESI). Despite varying the thermal treatment conditions, allu- audite materials were found to have an inherent tendency to form off-stoichiometric compositions. The environment of constituent iron in the intermedi- ate and annealed final materials was further gauged by room temperature Mössbauer analysis (Fig. 1, inset). The corresponding refined Mössbauer parameters [quadrupole splitting (∆), isomer shifts (δ), line width (Γ) and relative area (RA)] are given in Table 1. Despite synthesis in aque- ous media, no significant Fe oxidation was noticed with the Table 1 Mössbauer parameters of intermediate complex Na2Fe(SO4)2·4H2O (NFS1) and final material Na2+2xFe2−x(SO4)3 (NFS2) Sample Fe sites Quadrupole splitting (∆EQ) mm/s ± 0.008 Isomer shift (δ) mm/s ± 0.002 Line width (Г) mm/s ± 0.005 Relative Area, RA (%) Goodness of fit (χ2) NFS1 Doublet 1 (Fe2+) 3.266 1.248 0.267 61.3 1.008 Doublet 2 (Fe2+) 3.547 1.264 0.268 4.2 Doublet 3 (Fe2+) 1.722 1.186 0.250 4.5 Doublet 4 (Fe2+) 2.760 1.267 0.342 30.0 NFS2 Doublet 1 (Fe2+) 3.267 1.252 0.256 28.5 0.983 Doublet 2 (Fe3+) 0.478 0.368 0.445 7.0 Doublet 3 (Fe2+) 2.029 1.259 0.558 23.0 Doublet 4 (Fe2+) 2.708 1.260 0.357 41.5 Carbon coating Bulk alluaudite a) b) 1 μm 1 μm Intermediate Annealed Powder 2 nm Fig. 3 Microstructural insights into the spray-dried synthesized Na2.27Fe1.86(SO4)3 alluaudite. a SEM micrographs depicting the spherical morphology both (top) intermediate phase and (bottom) alluaudite phase. b Representative annular dark field HAADF image and the corresponding elemental mapping revealing nanospheres hav- ing uniform distribution of all constituent elements (Na, Fe, S, O). A thin ~ 2-nm carbon coating on alluaudite material was captured in TEM micrograph. High-resolution TEM image revealed the atomic fringes with interplanar distance of 0.284 nm (for (330) plane) attest- ing the crystallinity of the compound 1945Journal of Solid State Electrochemistry (2022) 26:1941–1950 1 3 materials consisting majorly Fe2+ species with minimal Fe3+ impurities. As Fe2+-based sulfate systems tend to oxidize, the addition of a pinch of ascorbic acid in precursor slurry can stabilize the Fe2+ environment in both the intermediate and final phase, as confirmed from Mössbauer analysis. Following, the morphology of spray-dried materials was examined using electron microscopy tools. SDS is a col- loidal/solution-assisted self-assembly process which leads to the rapid formation of droplets in presence of hot air. Thus, it leads to spherical morphology in the intermedi- ate as well as the final material as observed with the SEM images (Fig. 3a). A closer look at the surface morphology further suggests the as-annealed powder possessed rough and protrusion spherical exteriors with agglomeration. The high-angle annular dark-field imaging (HAADF) and TEM micrographs (Fig. 3b) further attest to the spherical mor- phology of the as-synthesized alluaudite depicting the rich nanospheres interconnected with carbon networks. The car- bon network/coating arises from the addition of a nominal amount of ascorbic acid in the precursor solution. High- resolution TEM pattern displayed good crystallinity with the indexed space group (C2/c). Energy-dispersive (EDS) elemental analysis confirmed homogeneous distribution of all selected elements: Na, Fe, S, O, and C. Further, an off- stoichiometric sodium-rich and iron-deficient environment was reaffirmed in sync with Rietveld (X-ray) analysis. Unlike the oxides and other polyanionic moieties (PO43−, MoO42−, SiO44−, etc.), the sulfates are intrinsically prone to moisture attack due to the Lewis basicity of oxygen atom in SO42− commensurate with that of H2O [25]. To gauge the effect of moisture on the as-prepared sample, FT-infrared 500 1000 1500 2000 2500 3000 3500 4000 30 40 50 60 70 80 90 100 Tr an sm itt an ce (% ) Wavelength (cm-1) Intermediate Powder Annealed Material SO42- bands OH peak (~ 3500 cm-1) ν1 ν2 ν3 ν1- asymmetric stretching ~1100 cm-1 ν2- symmetric stretching ~ 983 cm-1 ν3- asymmetric bending ~620 cm-1 Fig. 4 Comparative FT-infrared spectra of spray drying intermediate product and final alluaudite showing different vibrational bands aris- ing from constituent SO4 tetrahedral building blocks. The interme- diate product (hydrated bloedite) has a hump ~3400  cm−1, which is absent in case of the annealed (dehydrated alluaudite) material Fig. 5 a Variation in X-ray diffraction patterns of pristine alluau- dite subjected to different degree of relative humidity (10 ~ 90% of RH). While alluaudite phase was retained until RH 70%, a mixture of phases was noticed above that, which completely converted to hydrated bloedite above RH 88%. b Schematic presentation depicting alluaudite to bloedite phase transformation under influence of humid- ity. Exposure to humidity leads to the presence of structural water molecules and reorientation of FeO6 octahedral units to undergo all- uaudite to bloedite phase transition. c Depiction of reversible phase transition from alluaudite to bloedite (upon hydration) and bloedite to alluaudite (upon annealing) 1946 Journal of Solid State Electrochemistry (2022) 26:1941–1950 1 3 spectra of both spray dried powders and post annealed sam- ples were examined (Fig. 4). The intermediate complex showed a broad band ∼3500  cm−1 (related to symmetric/ asymmetric stretching of OH− species) revealing the pres- ence of structural water in bloedite composition. However, the post-annealed phase was found to have no residual H2O or surface-adsorbed moisture even though prepared via an aqueous route. Also, low wavenumber signature bands stemming from SO42− species were observed. Three dif- ferent kinds of infrared bands were captured: two from stretching vibration of SO4 units [asymmetric stretching ν1 ≈ 1100  cm−1 and symmetric stretching ν2 ≈ 983  cm−1] and one from bending vibration of SO4 units [asymmetric bending ν3 ≈ 620  cm−1]. The incorporation of thin carbon coating arising from carbon sources (ascorbic acid) was further verified by Raman spectroscopy, where signature D (∼1390  cm−1) and G (∼1595  cm−1) bands were captured arising from elemental carbon (Fig. S2, ESI). A relatively sharper G band hinted at the graphitic nature of the carbon coating, which can be beneficial for overall cathode electro- chemical performance. While the sulfate-based electrode materials offer high- voltage activity, they suffer from moisture-induced material instability during material storage/handling. Upon exposure to humidity, moisture-induced decomposition/phase transi- tion can occur, which is detrimental to the electrochemi- cal performance [26]. To gauge the stability, the effect of humidity on the structural stability of alluaudite type Na2.27Fe1.86(SO4)3 was probed by exposing the material in various RH (relative humidity) conditions using an X-ray diffractometer equipped with a sample chamber capable of controlling the relative humidity (RH-XRD). SDS-prepared alluaudite cathode was subjected to the humid environ- ment inside the sample chamber using an RH generator at room temperature. The evolution of the XRD patterns was recorded at different RH (10–90%) with 1 h of rest time during consecutive measurements. Upon varying the humid- ity percentage, a rapid disappearance of the Bragg peaks pertaining to the alluaudite phase was noticed with increas- ing humidity till 70% RH (Fig. 5a). Subsequently, a mixture of alluaudite and bloedite Na2Fe(SO4)2·4H2O was obtained at 75% RH. Above 85% RH, alluaudite Na2.27Fe1.86(SO4)3 phase was completely transformed to the bloedite Na2Fe(SO4)2·4H2O phase as illustrated in Fig. 5b. Unlike other sulfate-based insertion materials (e.g., fluorosulfates LiFeSO4F) leading to the formation of respective hydrated precursors (FeSO4·nH2O, with n = 1/4/7) upon moisture attack, a clear alluaudite to bloedite phase transition was noticed. It is interesting to note that this is exactly the reverse reaction of bloedite to alluaudite phase transition observed during the material synthesis (Fig. 1). Overall, alluaudite sulfate was found to be prone to moisture attack leading to the formation of hydrated derivatives. Thus, these cathode systems warrant careful storage inside an inert atmosphere. The ease and reversibility of alluaudite ↔ bloedite phase transition (Fig. 5c) inspired us to gauge the relative ther- modynamic stability of these phases using (thermochem- istry) calorimetric analysis. The solution calorimetric data Table 2 Calorimetric data of alluaudite Na2Fe2(SO4)3 and bloedite Na2Fe(SO4)2·4H2O Errors are two standard deviations of the mean. Values in parenthesis are the number of measurements Composition ΔHds (kJ/mol) ΔH°f (kJ/mol) Na2SO4 20.65 ± 0.40 (6) FeSO4 −35.44 ± 0.42 (5) [27] H2O −0.54 [28] Na2Fe2(SO4)3 −38.47 ± 0.84(7) −11.76 ± 1.25 Na2Fe(SO4)2·4H2O 100.21 ± 0.94(6) −117.16 ± 1.10 Table 3 Thermochemical cycles for enthalpy of formation for alluaudite Na2Fe2(SO4)3 and bloedite Na2Fe(SO4)2·4H2O Alluaudite Na2Fe2(SO4)3 Enthalpy measurement Na2Fe2(SO4)3 (s, 25 °C) + 6HCl (l, 25 °C) → 2NaCl (sln, 25 °C) + 2FeCl2 (sln, 25 °C) + 3H2SO4 (sln, 25 °C) ΔH1 = ΔHds [Na2Fe2(SO4)3] Na2SO4 (s, 25 °C) + 2HCl (l, 25 °C) → 2NaCl (sln, 25 °C) + H2SO4 (sln, 25 °C) ΔH2 = ΔHds (Na2SO4) FeSO4 (s, 25 °C) + 2HCl (l, 25 °C) → FeCl2 (sln, 25 °C) + H2SO4 (sln, 25 °C) ΔH3 = ΔHds (FeSO4) Na2SO4 (s, 25 °C) + FeSO4 (s, 25 °C) → Na2Fe2(SO4)3 (s, 25 °C) ΔH4 = ΔH°f [Na2Fe2(SO4)3] = − ΔH1 + ΔH2 + 2ΔH3 Bloedite Na2Fe(SO4)2·4H2O Enthalpy measurement Na2Fe(SO4)2·4H2O (s, 25 °C) + 4HCl (l, 25 °C) → 2NaCl (sln, 25 °C) + FeCl2 (sln, 25 °C) + 4H2O (sln, 25 °C) + 2H2SO4 (sln, 25 °C) ΔH5 = ΔHds [Na2Fe(SO4)2·4H2O] Na2SO4 (s, 25 °C) + 2HCl (l, 25 °C) → 2NaCl (sln, 25 °C) + H2SO4 (sln, 25 °C) ΔH2 = ΔHds (Na2SO4) FeSO4 (s, 25 °C) + 2HCl (l, 25 °C) → FeCl2 (sln, 25 °C) + H2SO4 (sln, 25 °C) ΔH3 = ΔHds (FeSO4) H2O (l,25 °C) → H2O (sln, 25 °C) ΔH6 = ΔHds (H2O) Na2SO4 (s, 25 °C) + FeSO4 (s, 25 °C) + 4H2O (l,25 °C) → Na2Fe(SO4)2·4H2O (s, 25 °C) ΔH7 = ΔH°f [Na2Cu(SO4)2·4H2O] = − ΔH5 + ΔH2 + ΔH3 + 4ΔH6 1947Journal of Solid State Electrochemistry (2022) 26:1941–1950 1 3 are shown in Table 2. The corresponding thermochemical cycles used to calculate heats of formation are shown in Table 3. While the alluaudite has a Na-rich and Fe-deficient nature, bloedite is always stoichiometric. Reactions must be mass balanced for calculating the formation enthalpy. Thus, we assume the composition of alluaudite to be stoi- chiometric, i.e., Na2Fe2(SO4)3, in the thermochemical cycles and dissolution enthalpy calculations. Any small deviations from stoichiometry are not known reliably and would not affect the calorimetric data significantly. The enthalpy of solution (ΔHds) for bloedite was calculated by subtracting the contribution from ΔHds(FeSO4), and the contributions from the minor secondary phases such as 1.92% FeSO4 and 1.01% Na6Fe(SO4)4 in the alluaudite were neglected since their contribution to ΔHds is < 2 kJ/mol. The enthalpies of solution (ΔHds) in 5 N HCl at 25 °C are −38.47 ± 0.84 kJ/mol for alluaudite and 100.21 ± 0.94 kJ/ mol for bloedite. The enthalpies of formation (ΔH°f) of alluaudite and bloedite from their constituent binary sul- fates, Na2SO4, and FeSO4 (plus H2O) were calculated using the thermochemical cycle in Table 3 and are exothermic. ΔH°f of bloedite is −117.16 ± 1.10 kJ/mol and that of allu- audite is −11.76 ± 1.25 kJ/mol, indicating that the hydrated Na2Fe(SO4)2 (bloedite) is significantly more energetically stable than the dehydrated Na2Fe2(SO4)3 (alluaudite). The calorimetric data support the observed synthesis and trans- formation (hydration-dehydration) pathways. The endothermic DSC signals at 75–200 °C are due to dehydration of bloedite, and the endothermic peak at 290 °C confirms the formation of the alluaudite phase. The weight change in the sample before and after the DSC measure- ments corresponds to the loss of 4 mol of H2O. The enthalpy of reaction (ΔH°rxn) of alluaudite and water to form bloedite and FeSO4 is calculated using the thermochemical cycle to be −105.52 ± 1.80 kJ/mol (Table 4). This exothermic reac- tion is the driving force for the formation of bloedite which Table 4 Thermochemical cycles for enthalpy of reaction (ΔH°rxn) of alluaudite and water to form bloedite and iron sulfate a NBS Tables [29] b US Geological Survey [30] Reactions Enthalpies (kJ/mol) Fe (s, 25 °C) + S (s, 25 °C) + 2O2 (g 25 °C) → FeSO4 (s, 25 °C) ΔH8 = −928.4a 2Na (s, 25 °C) + S (s, 25 °C) + 2O2 (g, 25 °C) → Na2SO4 (s, 25 °C) ΔH9 = −1387.8 ± 0.4b H2 (g, 25 °C) + 0.5O2 (g, 25 °C) → H2O (l, 25 °C) ΔH10 = −285.83 ± 0.1b Fe(s, 25 °C) + 2Na(s, 25 °C) + 2SO4 (s, 25 °C) + 4H2 (g, 25 °C) + 2O2 (g, 25 °C) → Na2Fe(SO4)2·4H2O ΔH11 = ΔH8 + ΔH9 + 4ΔH8 + ΔH7 = −3576.68 ± 1.17 2Fe(s, 25 °C) + 2Na(s, 25 °C) + 3SO4 (s, 25 °C) → Na2Fe2(SO4)3 ΔH12 = 2ΔH8 + ΔH9 + ΔH4 = −3256.36 ± 1.31 Na2Fe2(SO4)3(s, 25 °C) + 4H2O (l, 25 °C) → Na2Fe(SO4)2·4H2O (s, 25 °C) + FeSO4 (s, 25 °C) ΔH°rxn = ΔH13 = ΔH11 + ΔH8 − ΔH12 −4 ΔH10 = −105.52 ± 1.80 Fig. 6 Galvanostatic charge–discharge profiles of Na2.27Fe1.86(SO4)3 synthesized by spray drying method at a rate of C/20 (2Na in 20 h) at 25 °C. (Inset, left) Correspond- ing dQ/dV plot showing three distinct broad redox peaks with average potential located at 3.7–3.8 V (vs. Na/Na+). (Inset, right) Cycling stability and Coulombic efficiency for the first 30 cycles 0 20 40 60 80 100 120 1 2 3 4 5 6 7 8 Vo lta ge (V ) Specific Capacity (mAh/g) 2.8 3.2 3.6 4.0 4.4 -2 -1 0 1 2 Cell Potential (V) dQ /d V (a .u ) O1 O2 O3 R1 R2 R3 0 5 10 15 20 25 30 0 40 80 120 Cycle no. Sp ec ifi c C ap ac ity (m Ah /g ) 0 40 80 120 C ou lo m bi c Ef fic ie nc y( % ) 4th- 2nd cycle10th cycle30th- 25th cycle 1948 Journal of Solid State Electrochemistry (2022) 26:1941–1950 1 3 is the more stable phase. Thus, the thermochemical data con- firm sulfates readily react with water to form their hydrated derivative products. This thermodynamically driven water reactivity may present a problem in their application in bat- teries making inert storage essential. Finally, the electrochemical activity of spray drying pre- pared alluaudite Na2.27Fe1.86(SO4)3 was checked as a cathode material in a Na-ion half-cell architecture without any par- ticle size optimization or additional carbon nano-painting. The room-temperature galvanostatic charge–discharge pro- file showed a reversible sodium (de)insertion with a revers- ible discharge capacity of ~77 mAh/g (Fig. 6) at a rate of C/20, which is ~80% of the theoretical capacity (QTH = 100 mAh/g). After 30 cycles, the specific capacity decreased to 62 mAh/g. From the dQ/dV curve (Fig. 6, inset), three sets of broad redox peaks were clearly visible at around 3.3 V, 3.7 V, and 4.0 V, leading to the nominal redox poten- tial ~3.8 V (vs. Na/Na+). Without any cathode optimization, this desirable electrochemical activity could be attributed to the inherent open framework of alluaudites. Further, the addition of ascorbic acid as a carbon source and complexing agent and the nanometric-rich spherical morphology ren- dered the initial microstructural advantage to the cathodic performance. With further cathode optimization and suitable choice of electrolytes (and additives), the electrochemical activity of spray drying prepared alluaudite can be further improved. Conclusions In summary, this work demonstrates the aqueous- based two-step spray drying synthesis of alluaudite Na2+2xFe2−x(SO4)3 sodium insertion material. The pres- ence of liquid media assures atomic-level mixing and easy ionic diffusion, facilitating alluaudite formation with shorter annealing. Solution calorimetry confirmed that hydrated Na2Fe(SO4)2 (i.e., bloedite) is substan- tially more energetically stable than the dehydrated phase assemblage containing alluaudite Na2Fe2(SO4)3. Thus, hydration is strongly thermodynamically driven and may be a limitation in using alluaudite for battery applications. The calorimetric data support the observed synthesis and transformation (hydration-dehydration) pathways. It is once again proved that sulfate-based materials need to be handled carefully to prevent moisture attack by providing a detailed analysis on how the alluaudite phase completely changes to the bloedite phase on raiding relative humidity. The spray drying–made alluaudite material was found to deliver reversible high-voltage (ca. 3.8 V) operation with- out any material optimization. Spray drying route can be extended to the scalable economic preparation of various sulfate classes of polyanionic battery insertion materials. Supplementary information The online version contains supplemen- tary material available at https:// doi. org/ 10. 1007/ s10008- 022- 05142-w. Funding Open Access funding enabled and organized by Projekt DEAL. The Science and Engineering Research Broad (SERB, Govt. of India) provided financial support under the Early Career Research Award (ECR/2015/000525). The first author (PB) received from the Department of Science and Technology (DST) an INSPIRE fellowship (IF180127). DD received from the International Centre for Diffrac- tion Data (ICDD, USA) a Ludo Frevel crystallography fellowship and from the Electrochemical Society (ECS, USA) an H.H. Uhlig Sum- mer Fellowship. A.N. and K.J. received financial support from the U.S. Department of Energy, Office of Basic Energy Sciences, Grant DE-FG02-03ER46053. Declarations Competing interests The authors declare no competing interests. Open Access This article is licensed under a Creative Commons Attri- bution 4.0 International License, which permits use, sharing, adapta- tion, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http:// creat iveco mmons. org/ licen ses/ by/4. 0/. References 1. Yabuuchi N, Kubota K, Dahbi M, Komaba S (2014) Research development on sodium-ion batteries. Chem Rev 114:11636–11682 2. Manthiram A, Goodenough JB (1989) Lithium insertion into Fe2(SO4)3 frameworks. J Power Sources 26:403–408 3. Barpanda P (2016) Pursuit of sustainable iron-based sodium battery cathodes: two case studies. Chem Mater 28:1006–1011 4. Barpanda P, Lander L, Nishimura S, Yamada A (2018) Pol- yanionic insertion materials for sodium-ion batteries. Adv Energy Mater 8:1703055 5. Padhi AK, Nanjundaswamy KS, Goodenough JB (1997) Phos- pho-olivines as positive-electrode materials for rechargeable lithium batteries. J Electrochem Soc 144:1188–1194 6. Barpanda P, Oyama G, Nishimura S, Chung SC, Yamada A (2014) A 3.8-V earth-abundant sodium battery electrode. Nat Commun 5:4358 7. Fisher DJ (1955) Alluaudite. Am Min 40:1100–1109 8. Dwibedi D, Barpanda P, Yamada A (2020) Alluaudite battery cathodes. Small. Methods 4:2000051 9. Trad K, Carlier D, Croguennec L, Wattiaux A, Ben Amara M, Delmas C (2010) NaMnFe2(PO4)3 alluaudite phase: synthesis, structure, and electrochemical properties as positive electrode in lithium and sodium batteries. Chem Mater 22:5554–5562 10. Dwibedi D, Araujo RB, Chakraborty S, Shanbogh PP, Sundaram NG, Ahuja R, Barpanda P (2015) Na2.44Mn1.79(SO4)3: a new member of the alluaudite family of insertion compounds for sodium ion batteries. J Mater Chem A 3:18564–18571 11. Dwibedi D, Gond R, Dayamani A, Araujo RB, Chakraborty S, Ahuja R, Barpanda P (2017) Na2.32Co1.84(SO4)3 as a new 1949Journal of Solid State Electrochemistry (2022) 26:1941–1950 1 3 member of the alluaudite family of high-voltage sodium battery cathodes. Dalton Trans 46:55–63 12. Ming J, Barpanda P, Nishimura S, Okubo M, Yamada A (2015) An alluaudite Na2+2xFe2−X(SO4)3 (x=0.2) derivative phase as insertion host for lithium battery. Electrochem Commun 51:19–22 13. Oyama G, Nishimura S, Suzuki Y, Okubo M, Yamada A (2015) Off-stoichiometry in alluaudite-type sodium iron sulfate Na2+2xFe2−X(SO4)3 as an advanced sodium battery cathode mate- rial. ChemElectroChem 2:1019–1023 14. Dwibedi D, Ling CD, Araujo RB, Chakraborty S, Duraisamy S, Munichandraiah N, Ahuja R, Barpanda P (2016) Ionothermal synthesis of high-voltage alluaudite Na2+2xFe2−X(SO4)3 sodium insertion compound: Structural, electronic, and magnetic insights. ACS Appl Mater Interfaces 8:6982–6991 15. Dwibedi D, Baskar S, Barpanda P (2017) Sustainable aqueous synthesis and electrochemical insights on high-voltage sodium alluaudite insertion materials. ECS Trans 80:337–342 16. Rahaman MN (2017) Ceramic Processing and Sintering. CRC Press 17. Rietveld H (1969) A profile refinement method for nuclear and magnetic structures. J Appl Crystallogr 2:65–71 18. Larson A, Von Dreele R (2000) Report Laur 86–748. Los Alamos National Laboratory, New Mexico, USA 19. Toby B (2001) Expgui, a graphical user interface for Gsas. J Appl Crystallogr 34:210–213 20. Momma K, Izumi F (2008) Vesta: a three-dimensional visualiza- tion system for electronic and structural analysis. J Appl Crystal- logr 41:653–658 21. Kilday MV (1980) The enthalpy of solution of srm 1655 (KCl) in H2O. J Res Natl Bur Stand (US) 85:467 22. Zones SI, Jayanthi K, Pascual J, Xie D, Navrotsky A (2021) Ener- getics of the local environment of structure-directing agents influ- ence zeolite synthesis. Chem Mater 33:2126–2138 23. Meng Y, Yu T, Zhang S, Deng C (2016) Top-down synthesis of muscle-inspired alluaudite Na2+2xFe2−X(SO4)3/SWNT spindle as a high-rate and high-potential cathode for sodium-ion batteries. J Mater Chem A 4:1624–1631 24. Mineralogical database (2000) http:// www. mindat. org 25. Singh S, Jha PK, Avdeev M, Zhang W, Jayanthi K, Navrotsky A, Alshareef HN, Barpanda P (2021) Marinite Li2Ni(SO4)2 as a new member of the bisulfate family of high-voltage lithium battery cathodes. Chem Mater 33:6108–6119 26. Zhang L, Tarascon JM, Sougrati MT, Rousse G, Chen G (2015) Influence of relative humidity on the structure and electrochemi- cal performance of sustainable LiFeSO4F electrodes for Li-ion batteries. J Mater Chem A 3:16988–16997 27. Radha A, Lander L, Rousse G, Tarascon JM, Navrotsky A (2015) Thermodynamic stability and correlation with synthesis condi- tions, structure and phase transformations in orthorhombic and monoclinic Li2M(SO4)2 (M= Mn, Fe Co, Ni) polymorphs. J Mater Chem A 3:2601–2608 28. Parker VB (1965) National standard reference data series, National Bureau of Standards. 2:66 29. Wagman DD, Evans WH, Parker VB, Schumm RH, Halow I, Bailey SM, Churney KL, Nuttall RL (1982) The NBS tables of chemical thermodynamic properties. J Phys Chem Ref Data Suppl 2 National Bureau of Standards, Washington DC 20234, 177. 11:1807–1812 30. Robie R, Hemingway B (1995) Thermodynamic properties of minerals and related substances at 298.15 K and 1 bar (105 Pas- cals) and at higher temperatures. Bull US Geol Surv 2131:461 Publisher's Note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations. 1950 Journal of Solid State Electrochemistry (2022) 26:1941–1950